Effect of MicroArea pH Value on Formation of Different Rust Phases of Weathering Steel in Initial Corrosion Period

CHEN Xiaoping , WANG Xiangdong , LIU Qingyou , MI Fengyi , CHEN Ying , LI Yusu

钢铁研究学报(英文版)

The formation of protective rust layer of atmospheric corrosion resistance was discussed for weathering steel. The Rust layers of experimental steels were made by using an accelerating industrial atmospheric corrosion test of dry-wet cyclic immersion. Furthermore XRD were used to measure and analyze the rust layers. The initial corrosion processes below thin water film were observed and the changes of micro-area PH value were measured. The results are as follows: The corrosion processes are obviously different between P-RE weathering steel and carbon steel. The surface of P-RE weathering steel rapidly forms α-FeOOH and the micro-area PH value is above 5.4 during the initial corrosion period. While the component of the rust layer for the carbon steel is mainly Fe3O4 and the micro-area PH value is below 3.8.

关键词: weathering steel;pH value;micro area;rust phase

出版年份

刊物分类

相关作者

相关热词